Application of Jet Emitters for Nanofiber Production

By AZoM.com Staff Writers

Table of Content

Introduction
Why Jets are as Capillaries
Jet Design for Production of Nanofibre Materials:
Capillary Jets for Nanomaterial Production
Needleless Nanofibre Emitters
Needleless Multi-Jet Technology
About Contipro Group

Introduction

Using a nanofibre structure, a polymer solution is transformed into solid materials with electrospinning. The requirements are a solution of optimal physico-chemical properties, two electrodes connected to a high voltage source and a deposition chamber with controlled environmental conditions. Using electrostatic forces, individual fibres are formed from the surface of the polymer mixture. For the Taylor cone to be formed and the polymer to spurt, external electrostatic forces must be greater than the cohesive and capillary forces in the liquid.

Why Jets are as Capillaries

The curvature of the polymer mixture due to the jet shape supports the formation of the Taylor cone. The small radius of the surface curvature forms larger capillary forces, which increase pressure in the drop and strive to break the surface layer and thus the drop itself.

For electrospinning it is best to use a thin capillary, into which the polymer mixture is injected. The polymer mixture forms into minute droplets at the mouth of the capillary. Hence the mixture spurts even when the electrostatic forces are weaker. This is also beneficial when launching the process with polymer mixtures that are difficult to spin. The basic principle and most commonly used jet principle is therefore a thin hollow needle combined with continuous dosing of the polymer mixture, which is injected into the jet by force. Figure 1 shows droplets on the 4SPIN multi-jet emitter.

Figure 1. Droplets on the 4SPIN multi-jet emitter.

Jet Design for Production of Nanofibre Materials:

The emitters are designed to cover the following three functions:

  • The conductive feeding of high voltage
  • The continuous dosing of the spinning mixture
  • Its natural formation into the shape of a droplet. 

From the viewpoint of the production volume and in terms of functional capacity to turn the spinning mixture into nanofiber form, per unit of time, the technical design of the emitter is important i.e. the transformation of the maximum amount of spinning mixture into nanofiber form per unit of time. These two properties are, however, mutually contradictory. Figure 2 shows the continuous dosing system of a spinning mixture.

Figure 2. Continuous dosing system of a spinning mixture. 

Jet geometry is based on productivity and spinnability. The mixture needs to be naturally shaped into very small droplets subject to the strongest possible electrostatic forces for quality spinning. For productive emitters, however, the largest amount of mixture needs to be delivered.

Capillary Jets for Nanomaterial Production

The thin capillary jet is the first known spinning jet. A droplet of spinning mixture, from which fibre is generated by electrostatic forces, is continuously produced at the mouth of the thin capillary needle. This emitter type can create fiber from a mixture because of the fact that at the capillary mouth, a very small drop of the mixture (with a minimum curvature radius) is created, and the electrostatic field gradient exerts an extremely strong electrostatic force action on the spinning mixture. The droplet “succumbs” to these forces, forming a Taylor cone and creating a flying strand of fibre. Figure 3 shows the thin capillary needle jets.

Figure 3. Thin capillary needle jets.

This jet is mainly used in the early stages of laboratory development. A visible layer is spun slowly onto a small surface from the jet only after a few minutes of spinning, and a self-supporting layer of nanofibres takes several tens of minutes to form, depending on the solution. For increasing productivity, the number of capillary needles can be multiplied. At higher multiples (including 200 to 300 units), capillary jets can be used for larger-scale production. The main disadvantages include this equipment becoming easily clogged and are very difficult to clean, which significantly complicates the production process.

Needleless Nanofibre Emitters

In these cases, the Taylor cone is formed directly on the free surface of the polymer mixture, or from larger droplets which assume a natural shape on a smaller surface area of the spinning electrode. The basis of these needleless systems includes the original patents (from 1934 and 1936) combined with the current ES method for the preparation of nanofibres and microfibres.

These jets are in the shape of a container filled with a polymer mixture, in which a rotating cylinder is partially immersed. Cylinder rotation causes the polymer mixture to be scooped onto the surface of the cylinder. 

The key factor here and an impediment to larger-scale production is the change in solution properties during the spinning process, as this takes place in open climate conditions, where solution components evaporate naturally, meaning that the changes in the solution’s physico-chemical parameters are uncontrolled. There is also a much smaller electrostatic field gradient on the surface of the needleless jet and the external electrostatic forces are too weak to launch the spinning process.

Needleless Multi-Jet Technology

All disadvantages of needleless spinning electrodes are eliminated by the design of the spinning needleless multi-jets. The relatively large quantity of spinning mixture is dosed through internal distribution channels to the thin edge of the conductive electrode. At the mouth of the channel on this edge, the spinning mixture naturally takes the form of a droplet, which leads to spinning. As a result, when a needleless multi-jet is used, the greatest productivity yet is achieved, while maintaining high spinnability. Figure 4 and 5 show the needleless multi-jet spinning electrodes and electrospinning from a multi-jet emitter.

Figure 4. Needleless multi-jet spinning electrodes.

Figure 5. Electrospinning from a multi-jet emitter.

The closed dosing system ensures long-term constant parameters for the polymer mixture used to make the resulting nanomaterial. The technical needleless multi-jet design (patented by Contipro) and used in a number of devices in the 4SPIN series is suitable for pilot/operational production of nanomaterials, is easy to clean and can cover a large area with nanomaterial on the collector.

About Contipro Group

The CONTIPRO holding has been involved in the research, development and biotechnological production of active ingredients for the cosmetic and pharmaceutical industries for over twenty years. With excellent production quality and extensive research facilities, it is one of the world’s leading manufacturers of hyaluronic acid and derived applications.

The holding places a huge emphasis on innovation and in-house research, which explains why almost half of its employees are R&D laboratory experts.

The oldest of the holding’s companies, Contipro Pharma, specializes in the manufacture of sodium hyaluronate pharmaceutical grade and other active substances for the pharmaceutical industry and finished pharmaceutical products made from hyaluronic acid.

Contipro Biotech, which produces hyaluronic acid cosmetic grade and other active ingredients for products to counter the effects of skin ageing, was founded in 1997.

This information has been sourced, reviewed and adapted from materials provided by Contipro Group.

For more information on this source, please visit Contipro Group.